Plastic Material Specs ISO9001

Select the name of the material below you would like to review the specifications for.
ABS Kydex Polystyrene
Acetals Linen Phenolic PVC
Acrylic Nomex Tectron
Canvas Phenolic Nylatron Teflon All
Duratron Polyimide Nylon Torlon
G10 Peek-All UHMW
Glass Thermosets Phenolics Ultem
GPO Materials Polycarbonate Vespel
HDPE Polypro  

 

 

 

 

 

 

 

 

 

 

 

 

 

ABS Specs
- -
Units
ASTM Test Method
Acrylonitrile Butadiene Styrene
MECHANICAL
Strength to Weight Ratio ksi - 5.3
Specific Gravity @73 F - D792 1.04
Tensile Strength @73 F, (ult)/(yld) psi D638 5500 (ult)
Tensile Modulus of Elasticity @ 73 F psi D638 346000
Tensile Elongation at Break @ 73 F % D638 20
Flexural Strength @ 73 F psi D790 9300
Flexural Modulus of Elasticity @ 73 F psi D790 340000
Shear Strength @ 73 F psi D732 -
Compressive Strength, (% Deformation) @73 F psi D695 -
Compressive Modulus of Elasticity @73 F psi D695 -
Hardness, Rockwell, Scale as noted @73 F - D785 (R105)
Hardness, Durometer, Shore D @73 F - D2240 -
Izod Impact, (Notched) @73 F ft-lb/in of notch D256 TypeA 7.0
Coefficient of Friction, (Dry vs. Steel) Dynamic - - 0.35
Limiting PV, (with 4 to 1 factor of safety applied) psi-ft/min - -
THERMAL
Coefficient of Linear Thermal Expansion @73 F in/in/F E-831 (TMA) 5.2E-05
Heat Deflection Temperature @ 264 psi F D648 220
Tg-Glass transition temperature, (Amorphous) F D3418 -
Melting Point, (VS=Vicat Softening Temp.) F D3418 220
Continuous Service Temperature in Air, (Max.) F - 160
Thermal Conductivity BTU-in/hr-ft2-F - 1.18
ELECTRICAL
Dielectric Strength, Short Term Volts/mil D149 450
Volume Resistivity ohm-cm D257 1.0E+15
Dielectric Constant @ 10E6 Hz - D150 -
Dissipation Factor @ 10E6 Hz - D150 -
Flammability @ 3.1 mm unless noted - UL94 HB (6.10mm)
H2O
Water Absorbtion, Immersion, 24 Hrs % by wt. D570(7) 0.30
Water Absorbtion, Saturation % by wt. D570(7) 0.70

Back to Top

 

 

Acetals Specs
        Acetron GP Acetal Delrin Acetal Delrin 570 Blend 25% Glass-Filled Acetal Copolymer Delrin AF Filled Acetal Acetron NS Filled Acetal Delrin 500 CL
    Units ASTM Test Method Poly-oxymethylene Copolymer Poly-oxymethylene Homopolymer 20% Glass Filled POM Homopolymer 25% Glass Filled POM Copolymer PTFE Filled POM Homopolymer Lubricated POM Copolymer Lubricated POM Homopolymer
MECHANICAL
Strength to Weight Ratio
ksi
-
-
-
-
-
-
-
-
Specific Gravity @73 F
-
D792
1.41
1.41
1.56
1.59
1.50
1.44
1.42
Tensile Strength @73 F, (ult)/(yld)
psi
D638
9500 (ult)
11000 (ult)
8500 (ult)
16000(yld)
8000 (ult)
7500 (ult)
9500 (yld)
Tensile Modulus of Elasticity @ 73 F
psi
D638
400000
450000
900000
1200000
435000
400000
450000
Tensile Elongation at Break @ 73 F
%
D638
30
30
12
2-3%
15
10
40
Flexural Strength @ 73 F
psi
D790
12000
13000
10700
-
12000
15000
13000
Flexural Modulus of Elasticity @ 73 F
psi
D790
400000
450000
730000
1050000
445000
400000
400000
Shear Strength @ 73 F
psi
D732
8000
9000
-
-
7600
6000
-
Compressive Strength, (% Deformation) @73 F
psi
D695
15000 (10)
16000 (10)
-
-
16000 (10)
15000 (10)
4500 (1)
Compressive Modulus of Elasticity @73 F
psi
D695
400000
450000
-
-
350000
315000
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M88 (R120)
m89 (R122)
M90 (R118)
M80
M85 (R115)
M85 (R116)
M90 (R120)
Hardness, Durometer, Shore D @73 F
-
D2240
D85
D86
-
-
D83
D83
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
1.0
1.0
0.8
1.1
0.7
0.7
1.4
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
0.25
0.25
0.34
-
0.19
0.20
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
2700
2700
-
-
7500
7500
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
5.4E-04
4.7E-05
4.5E-05
2.2E-05
5.0E-05
4.7E-05
6.8E-05
Heat Deflection Temperature @ 264 psi
F
D648
220
250
316
322
244
250
257
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
-
-
-
-
-
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
335
347
347
-
347
347
347
Continuous Service Temperature in Air, (Max.)
F
-
180
180
185
-
180
180
-
Thermal Conductivity
BTU-in/hr-ft2-F
-
1.60
2.50
-
-
-
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
420
450
490
-
400
350
400
Volume Resistivity
ohm-cm
D257
1.0E+17
1.0E+15
5.0E+14
-
3.0E+16
1.0E+15
1.0E+15
Dielectric Constant @ 10E6 Hz
-
D150
3.8
3.7
-
-
3.1
-
3.5
Dissipation Factor @ 10E6 Hz
-
D150
0.005
0.005
0.006
-
0.010
-
0.006
Flammability @ 3.1 mm unless noted
-
UL94
HB
HB
HB
-
HB
HB
HB (.78mm)
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
0.20
0.20
0.25
0.29
0.20
0.20
0.27
Water Absorbtion, Saturation
% by wt.
D570(7)
0.90
0.90
1.00
-
1.0
0.90
0.90

Back to Top

 

 

Acrylic Specs
 
 
 
 
C, CE
 
 
Units
ASTM Test Method
Canvas Phenolic
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
1.35
Tensile Strength @73 F, (ult)/(yld)
psi
D638
9500
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
Tensile Elongation at Break @ 73 F
%
D638
-
Flexural Strength @ 73 F
psi
D790
17000
Flexural Modulus of Elasticity @ 73 F
psi
D790
950000
Shear Strength @ 73 F
psi
D732
11500
Compressive Strength, (% Deformation) @73 F
psi
D695
37000 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M104
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
3.2/2.3
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
Heat Deflection Temperature @ 264 psi
F
D648
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
265
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
150/360
Volume Resistivity
ohm-cm
D257
-
Dielectric Constant @ 10E6 Hz
-
D150
-,5.8
Dissipation Factor @ 10E6 Hz
-
D150
.1,.055
Flammability @ 3.1 mm unless noted
-
UL94
HB
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
1.2,.75
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

 


Canvas Phenolic Specs
 
 
 
 
C, CE
 
 
Units
ASTM Test Method
Canvas Phenolic
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
1.35
Tensile Strength @73 F, (ult)/(yld)
psi
D638
9500
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
Tensile Elongation at Break @ 73 F
%
D638
-
Flexural Strength @ 73 F
psi
D790
17000
Flexural Modulus of Elasticity @ 73 F
psi
D790
950000
Shear Strength @ 73 F
psi
D732
11500
Compressive Strength, (% Deformation) @73 F
psi
D695
37000 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M104
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
3.2/2.3
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
Heat Deflection Temperature @ 264 psi
F
D648
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
265
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
150/360
Volume Resistivity
ohm-cm
D257
-
Dielectric Constant @ 10E6 Hz
-
D150
-,5.8
Dissipation Factor @ 10E6 Hz
-
D150
.1,.055
Flammability @ 3.1 mm unless noted
-
UL94
HB
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
1.2,.75
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top


 

Duratron Polyimide Specs
 
 
 
 
Duratron HP
 
 
Units
ASTM Test Method
High Purity Polyimide
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
1.34
Tensile Strength @73 F, (ult)/(yld)
psi
D638
13500 (ult)
Tensile Modulus of Elasticity @ 73 F
psi
D638
578000
Tensile Elongation at Break @ 73 F
%
D638
3
Flexural Strength @ 73 F
psi
D790
23000
Flexural Modulus of Elasticity @ 73 F
psi
D790
530000
Shear Strength @ 73 F
psi
D732
-
Compressive Strength, (% Deformation) @73 F
psi
D695
19000 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
410000
Hardness, Rockwell, Scale as noted @73 F
-
D785
M120
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
0.6
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
0.23
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
32500
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
2.0E-05
Heat Deflection Temperature @ 264 psi
F
D648
592
Tg-Glass transition temperature, (Amorphous)
F
D3418
613
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
580
Thermal Conductivity
BTU-in/hr-ft2-F
-
1.53
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
-
Volume Resistivity
ohm-cm
D257
>1E14
Dielectric Constant @ 10E6 Hz
-
D150
-
Dissipation Factor @ 10E6 Hz
-
D150
-
Flammability @ 3.1 mm unless noted
-
UL94
V-0
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
0.62
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

 

 

G10 Specs
 
 
 
 
G10, FR4
 
 
Units
ASTM Test Method
Glass cloth Reinforced Epoxy
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
1.82
Tensile Strength @73 F, (ult)/(yld)
psi
D638
40000
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
Tensile Elongation at Break @ 73 F
%
D638
-
Flexural Strength @ 73 F
psi
D790
55000
Flexural Modulus of Elasticity @ 73 F
psi
D790
2700000
Shear Strength @ 73 F
psi
D732
19000
Compressive Strength, (% Deformation) @73 F
psi
D695
60000 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M110
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
7.0
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
Heat Deflection Temperature @ 264 psi
F
D648
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
285
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
400
Volume Resistivity
ohm-cm
D257
-
Dielectric Constant @ 10E6 Hz
-
D150
5.2
Dissipation Factor @ 10E6 Hz
-
D150
0.025
Flammability @ 3.1 mm unless noted
-
UL94
V-O
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
0.10
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

 

 

Glass Thermosets Specs
 
 
 
 
G10, FR4
G5, G9
G7
 
 
Units
ASTM Test Method
Glass cloth Reinforced Epoxy
Glass cloth Reinforced Melamine
Glass Cloth Reinforced Silicone
MECHANICAL
Strength to Weight Ratio
ksi
-
 
 
 
Specific Gravity @73 F
-
D792
1.82
1.9
1.68
Tensile Strength @73 F, (ult)/(yld)
psi
D638
40000
37000
23000
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
-
-
Tensile Elongation at Break @ 73 F
%
D638
-
-
-
Flexural Strength @ 73 F
psi
D790
55000
55000
23000
Flexural Modulus of Elasticity @ 73 F
psi
D790
2700000
2500000
1400000
Shear Strength @ 73 F
psi
D732
19000
20000
17000
Compressive Strength, (% Deformation) @73 F
psi
D695
60000 (10)
70000 (10)
45000 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
-
-
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M110
M120
M100
Hardness, Durometer, Shore D @73 F
-
D2240
-
-
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
7.0
12.0
8.5
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
-
-
Heat Deflection Temperature @ 264 psi
F
D648
-
-
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
-
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
-
-
Continuous Service Temperature in Air, (Max.)
F
-
285
285
465
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
400
350
350
Volume Resistivity
ohm-cm
D257
-
-
-
Dielectric Constant @ 10E6 Hz
-
D150
5.2
7.1
4.2
Dissipation Factor @ 10E6 Hz
-
D150
0.025
0.017
0.003
Flammability @ 3.1 mm unless noted
-
UL94
V-O
V-O
V-O
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
0.10
0.40
0.15
Water Absorbtion, Saturation
% by wt.
D570(7)
-
-
-

Back to Top

 

 

GPO Materials Specs
 
 
 
 
Lamicor Grade GP-9105
Lamicor Grade GP-9206
Lamicor Grade GP-9306
Lamicor Grade CP-200 HT
 
 
Units
ASTM Test Method
Polyester - Glass Laminate (GPO-1)
FR Polyester Glass Laminate (GPO-2)
FR Polyester Glass Laminate (GPO-3)
High Temperature Polyester Glass Laminate
MECHANICAL
Strength to Weight Ratio
ksi
-
 
 
 
 
Specific Gravity @73 F
-
D792
1.95
1.80
1.80
1.77
Tensile Strength @73 F, (ult)/(yld)
psi
D638
9000
9000
9000
15000
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
-
-
-
Tensile Elongation at Break @ 73 F
%
D638
 
-
-
-
Flexural Strength @ 73 F
psi
D790
21000
21000
21500
28000
Flexural Modulus of Elasticity @ 73 F
psi
D790
-
-
-
-
Shear Strength @ 73 F
psi
D732
-
-
-
-
Compressive Strength, (% Deformation) @73 F
psi
D695
30000
30000
33000
28000
Compressive Modulus of Elasticity @73 F
psi
D695
 
-
-
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M-112
M-105
M-105
M101
Hardness, Durometer, Shore D @73 F
-
D2240
-
-
-
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
-
8.2
8.3
14
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
-
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
-
-
-
Heat Deflection Temperature @ 264 psi
F
D648
-
-
-
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
-
-
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
-
-
-
Continuous Service Temperature in Air, (Max.)
F
-
266
311
284
392
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
-
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
400
400
400
380
Volume Resistivity
ohm-cm
D257
-
-
-
-
Dielectric Constant @ 10E6 Hz
-
D150
4.5
4.95
4.1
4.10
Dissipation Factor @ 10E6 Hz
-
D150
.01
.02
.027
0.07
Flammability @ 3.1 mm unless noted
-
UL94
-
V-0
V-0
-
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
-
.13
0.12
0.25
Water Absorbtion, Saturation
% by wt.
D570(7)
-
-
-
-

Back to Top

 

 

HDPE Specs
 
 
 
 
HDPE
 
 
Units
ASTM Test Method
High Density Polyehylene
MECHANICAL
Strength to Weight Ratio
ksi
-
4.9
Specific Gravity @73 F
-
D792
0.94
Tensile Strength @73 F, (ult)/(yld)
psi
D638
4600 (ult)
Tensile Modulus of Elasticity @ 73 F
psi
D638
170000
Tensile Elongation at Break @ 73 F
%
D638
55
Flexural Strength @ 73 F
psi
D790
1400
Flexural Modulus of Elasticity @ 73 F
psi
D790
200000
Shear Strength @ 73 F
psi
D732
3380
Compressive Strength, (% Deformation) @73 F
psi
D695
4570 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
-
Hardness, Durometer, Shore D @73 F
-
D2240
D69
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
3.0
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
1.3E-04
Heat Deflection Temperature @ 264 psi
F
D648
151
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
180
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
500
Volume Resistivity
ohm-cm
D257
1.0E+15
Dielectric Constant @ 10E6 Hz
-
D150
-
Dissipation Factor @ 10E6 Hz
-
D150
-
Flammability @ 3.1 mm unless noted
-
UL94
-
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
0.03
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

 

 

Kydex Specs
 
 
 
 
Kydex 100
 
 
Units
ASTM Test Method
Acrylic/PVC Alloy Sheet
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
1.35
Tensile Strength @73 F, (ult)/(yld)
psi
D638
6100
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
Tensile Elongation at Break @ 73 F
%
D638
160
Flexural Strength @ 73 F
psi
D790
9300
Flexural Modulus of Elasticity @ 73 F
psi
D790
335000
Shear Strength @ 73 F
psi
D732
-
Compressive Strength, (% Deformation) @73 F
psi
D695
-
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
R-94
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
18 (953)
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
Heat Deflection Temperature @ 264 psi
F
D648
173
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
-
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
-
Volume Resistivity
ohm-cm
D257
-
Dielectric Constant @ 10E6 Hz
-
D150
-
Dissipation Factor @ 10E6 Hz
-
D150
-
Flammability @ 3.1 mm unless noted
-
UL94
V-0
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
-
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

 

Linen Phenolic Specs
 
 
 
 
L, LE
 
 
Units
ASTM Test Method
Linen Phenolic
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
1.34
Tensile Strength @73 F, (ult)/(yld)
psi
D638
12500
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
Tensile Elongation at Break @ 73 F
%
D638
-
Flexural Strength @ 73 F
psi
D790
15000
Flexural Modulus of Elasticity @ 73 F
psi
D790
1050000
Shear Strength @ 73 F
psi
D732
11750
Compressive Strength, (% Deformation) @73 F
psi
D695
37000 (10)
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
M105
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
2.5/1.8
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
Heat Deflection Temperature @ 264 psi
F
D648
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
265
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
150/360
Volume Resistivity
ohm-cm
D257
-
Dielectric Constant @ 10E6 Hz
-
D150
-,5.8
Dissipation Factor @ 10E6 Hz
-
D150
.1,.055
Flammability @ 3.1 mm unless noted
-
UL94
HB
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
.9,.7
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

 

Nomex Specs
 
 
 
 
Nomex Type 410
 
 
Units
ASTM Test Method
Aromatic Polyamide (Aramid) Paper
MECHANICAL
Strength to Weight Ratio
ksi
-
 
Specific Gravity @73 F
-
D792
0.7 - 1.2
Tensile Strength @73 F, (ult)/(yld)
psi
D638
548
Tensile Modulus of Elasticity @ 73 F
psi
D638
-
Tensile Elongation at Break @ 73 F
%
D638
-
Flexural Strength @ 73 F
psi
D790
-
Flexural Modulus of Elasticity @ 73 F
psi
D790
-
Shear Strength @ 73 F
psi
D732
-
Compressive Strength, (% Deformation) @73 F
psi
D695
-
Compressive Modulus of Elasticity @73 F
psi
D695
-
Hardness, Rockwell, Scale as noted @73 F
-
D785
-
Hardness, Durometer, Shore D @73 F
-
D2240
-
Izod Impact, (Notched) @73 F
ft-lb/in of notch
D256 TypeA
-
Coefficient of Friction, (Dry vs. Steel) Dynamic
-
-
-
Limiting PV, (with 4 to 1 factor of safety applied)
psi-ft/min
-
-
THERMAL
Coefficient of Linear Thermal Expansion @73 F
in/in/F
E-831 (TMA)
-
Heat Deflection Temperature @ 264 psi
F
D648
-
Tg-Glass transition temperature, (Amorphous)
F
D3418
-
Melting Point, (VS=Vicat Softening Temp.)
F
D3418
-
Continuous Service Temperature in Air, (Max.)
F
-
-
Thermal Conductivity
BTU-in/hr-ft2-F
-
-
ELECTRICAL
Dielectric Strength, Short Term
Volts/mil
D149
815
Volume Resistivity
ohm-cm
D257
2.0E+16
Dielectric Constant @ 10E6 Hz
-
D150
2.7
Dissipation Factor @ 10E6 Hz
-
D150
.006
Flammability @ 3.1 mm unless noted
-
UL94
-
H2O
Water Absorbtion, Immersion, 24 Hrs
% by wt.
D570(7)
-
Water Absorbtion, Saturation
% by wt.
D570(7)
-

Back to Top

Email
Tel: 856-767-3930
Fax: 856-767-3931
Copyright © 2009 JMJ Profile Inc., All rights reserved. Website by B2B Design & Development