Units
|
ASTM Test Method
|
Acrylonitrile Butadiene Styrene
|
|
MECHANICAL
|
Strength to Weight Ratio |
ksi |
– |
5.3 |
| Specific Gravity @73 F |
– |
D792 |
1.04 |
| Tensile Strength @73 F, (ult)/(yld) |
psi |
D638 |
5500 (ult) |
| Tensile Modulus of Elasticity @ 73 F |
psi |
D638 |
346000 |
| Tensile Elongation at Break @ 73 F |
% |
D638 |
20 |
| Flexural Strength @ 73 F |
psi |
D790 |
9300 |
| Flexural Modulus of Elasticity @ 73 F |
psi |
D790 |
340000 |
| Shear Strength @ 73 F |
psi |
D732 |
– |
| Compressive Strength, (% Deformation) @73 F |
psi |
D695 |
– |
| Compressive Modulus of Elasticity @73 F |
psi |
D695 |
– |
| Hardness, Rockwell, Scale as noted @73 F |
– |
D785 |
(R105) |
| Hardness, Durometer, Shore D @73 F |
– |
D2240 |
– |
| Izod Impact, (Notched) @73 F |
ft-lb/in of notch |
D256 TypeA |
7.0 |
| Coefficient of Friction, (Dry vs. Steel) Dynamic |
– |
– |
0.35 |
| Limiting PV, (with 4 to 1 factor of safety applied) |
psi-ft/min |
– |
– |
|
THERMAL
|
Coefficient of Linear Thermal Expansion @73 F |
in/in/F |
E-831 (TMA) |
5.2E-05 |
| Heat Deflection Temperature @ 264 psi |
F |
D648 |
220 |
| Tg-Glass transition temperature, (Amorphous) |
F |
D3418 |
– |
| Melting Point, (VS=Vicat Softening Temp.) |
F |
D3418 |
220 |
| Continuous Service Temperature in Air, (Max.) |
F |
– |
160 |
| Thermal Conductivity |
BTU-in/hr-ft2-F |
– |
1.18 |
|
ELECTRICAL
|
Dielectric Strength, Short Term |
Volts/mil |
D149 |
450 |
| Volume Resistivity |
ohm-cm |
D257 |
1.0E+15 |
| Dielectric Constant @ 10E6 Hz |
– |
D150 |
– |
| Dissipation Factor @ 10E6 Hz |
– |
D150 |
– |
| Flammability @ 3.1 mm unless noted |
– |
UL94 |
HB (6.10mm) |
|
|
Water Absorbtion, Immersion, 24 Hrs |
% by wt. |
D570(7) |
0.30 |
| Water Absorbtion, Saturation |
% by wt. |
D570(7) |
0.70 |